Methods for Manufacturing Delivery Systems and Systems Thereof

ABSTRACT

Described herein are methods for reducing and achieving the desired release of an agent from a delivery system. The desired release kinetics are achieved by exposing the surface of the delivery system with a fluid for a desired period of time.

CROSS REFERENCE TO RELATED APPLICATIONS

This application claims the benefit of U.S. Provisional Application Ser. No. 60/599,174, filed on Aug. 4, 2004, which application is hereby incorporated by reference in its entirety for all of its teachings.

BACKGROUND

In the realm of pharmaceutical formulations, there is a class of drug-delivery formulations that are designed to release bioactive agents for a desired period of time following a single administration. Depot formulation is one name used to describe these long-acting formulations. Depot formulations can be fabricated in many ways. A typical formulation approach to prepare a depot formulation or implant is by manufacturing a solid matrix that includes a bioactive agent and a polymeric excipient. The purpose of the polymeric excipient of the implant is to restrict the influx of water, which in turns controls the dissolution of the bioactive agent followed by the release of the bioactive agent from the implant matrix. In addition to the physical and chemical properties of the bioactive agent, the amount of bioactive agent in the implant contributes to the rate of bioactive agent release. That is, increasing the amount of bioactive agent increases the rate of release. Unfortunately, some implant formulations require a high amount of bioactive agent inside in order to have enough bioactive agent available to achieve dose and duration requirements for a particular medical indication. A high amount of bioactive agent incorporated inside the implant, however, may cause the release the bioactive agent to occur too fast or even at an uncontrollable rate.

It is an object of the present invention to provide delivery systems with a controlled release even at high loadings. Moreover, it is an object of the present invention to provide delivery systems and methods for their manufacture having decreased microbial contamination. It is a further object of the present invention to provide delivery systems having a smooth or smoother (than untreated) surface for easy administration. It is another object of the present invention to provide delivery systems where the delivery rate can be adjusted by modifying the surface.

The present invention solves this rapid release problem, i.e., the bioactive agent being released too fast, by modifying the polymeric surface or polymer skin of a delivery system by exposing the polymer present in the system to a fluid. The fluid-treatment causes the properties of the polymer on the surface of the delivery system to change such that the system is less permeable. It is the fluid treatment of the delivery system that is responsible for the slower release of the bioactive agent from the delivery system. In addition, the delivery systems produced herein are generally smoother than other delivery systems, which can facilitate the administration of the system to the subject. Additionally, the methods described herein can lower the bioburden of the delivery system by reducing the presence of microorganisms present on the system. Finally, the delivery systems produced herein have increased tensile strength, i.e., reduced friability, which aids in the preparation and administration of the system.

SUMMARY

Described herein are methods for reducing and achieving the desired release of an agent from a delivery system. The desired release kinetics are achieved by exposing the surface of the delivery system to a fluid for a predetermined period of time. The advantages of the invention will be set forth in part in the description which follows, and in part will be obvious from the description, or may be learned by practice of the aspects described below. The advantages described below will be realized and attained by means of the elements and combinations particularly pointed out in the appended claims. It is to be understood that both the foregoing general description and the following detailed description are exemplary and explanatory only and are not restrictive.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 shows the in vitro release of vitamin B₁₂ (45 wt %) from poly(DL-lactide) implants with and without fluid exposure.

FIG. 2 shows the in vitro release characteristics of Deslorelin implants (44 wt %) made with poly(DL-lactide) with and without fluid exposure.

FIG. 3 shows the in vitro release characteristics of Risperidone implants (50 wt %) made with poly(DL-lactide) with and without fluid exposure.

FIG. 4 shows the in vitro release of vitamin B₁₂ (50 wt %) from poly(DL-lactide) implants with and without fluid exposure.

FIG. 5 shows the in vitro release of vitamin B₁₂ (45 wt %) from ethyl vinyl acetate implants with and without fluid exposure.

DETAILED DESCRIPTION

Before the present compounds, compositions, and/or methods are disclosed and described, it is to be understood that the aspects described below are not limited to specific compounds, synthetic methods, or uses as such may, of course, vary. It is also to be understood that the terminology used herein is for the purpose of describing particular aspects only and is not intended to be limiting.

In this specification and in the claims that follow, reference will be made to a number of terms that shall be defined to have the following meanings:

Throughout this specification, unless the context requires otherwise, the word “comprise,” or variations such as “comprises” or “comprising,” will be understood to imply the inclusion of a stated integer or step or group of integers or steps but not the exclusion of any other integer or step or group of integers or steps.

It must be noted that, as used in the specification and the appended claims, the singular forms “a,” “an” and “the” include plural referents unless the context clearly dictates otherwise. Thus, for example, reference to “a pharmaceutical carrier” includes mixtures of two or more such carriers, and the like.

“Optional” or “optionally” means that the subsequently described event or circumstance can or cannot occur, and that the description includes instances where the event or circumstance occurs and instances where it does not.

Ranges may be expressed herein as from “about” one particular value, and/or to “about” another particular value. When such a range is expressed, another aspect includes from the one particular value and/or to the other particular value. Similarly, when values are expressed as approximations, by use of the antecedent “about,” it will be understood that the particular value forms another aspect. It will be further understood that the endpoints of each of the ranges are significant both in relation to the other endpoint, and independently of the other endpoint.

A weight percent of a component, unless specifically stated to the contrary, is based on the total weight of the formulation or composition in which the component is included.

By “contacting” is meant an instance of exposure by close physical contact of at least one substance to another substance.

By “combination” when referring to components of the polymer, it is meant a physical mixture (blend), a non-homogeneous mixture, multiple layers of the individual polymers, or a copolymer thereof.

The term “admixing” is defined as mixing the two components together. Depending upon the components to be admixed, there may or may not be a chemical or physical interaction between two or more components.

By “sufficient amount” and “sufficient time” means an amount and time needed to achieve the desired result or results.

Disclosed are compounds, compositions, and components that can be used for, can be used in conjunction with, can be used in preparation for, or are products of the disclosed methods and compositions. These and other materials are disclosed herein, and it is understood that when combinations, subsets, interactions, groups, etc. of these materials are disclosed that while specific reference of each various individual and collective combinations and permutation of these compounds may not be explicitly disclosed, each is specifically contemplated and described herein. For example, if a number of different polymers and agents are disclosed and discussed, each and every combination and permutation of the polymer and agent are specifically contemplated unless specifically indicated to the contrary. Thus, if a class of molecules A, B, and C are disclosed as well as a class of molecules D, E, and F and an example of a combination molecule, A-D is disclosed, then even if each is not individually recited, each is individually and collectively contemplated. Thus, in this example, each of the combinations A-E, A-F, B-D, B-E, B-F, C-D, C-E, and C-F are specifically contemplated and should be considered disclosed from disclosure of A, B, and C; D, E, and F; and the example combination A-D. Likewise, any subset or combination of these is also specifically contemplated and disclosed. Thus, for example, the sub-group of A-E, B-F, and C-E are specifically contemplated and should be considered disclosed from disclosure of A, B, and C; D, E, and F; and the example combination A-D. This concept applies to all aspects of this disclosure including, but not limited to, steps in methods of making and using the disclosed compositions. Thus, if there are a variety of additional steps that can be performed it is understood that each of these additional steps can be performed with any specific embodiment or combination of embodiments of the disclosed methods, and that each such combination is specifically contemplated and should be considered disclosed.

Described herein are methods for producing delivery systems. As used herein, “delivery systems” refer to both devices and coated articles as defined herein. The methods described herein allow for the manufacture of controlled-release, extended-release, modified-release, sustained-release, pulsatile-release, delayed-release, or programmed-release delivery of an agent. The term “delivery” as used herein includes all different types of delivery. In a further aspect, the delivery system is a device. In another further aspect, the delivery system is a coated article.

The term “device” is any formulation or article that is greater than 1 mm in length in at least one dimension of the device. The device can comprise a polymer and an agent. In a further aspect, the device has one dimension that is from 1 mm to 50 mm, 1.2 mm to 45 mm, 1.4 mm to 42 mm, 1.6 mm to 40 mm, 1.8 mm to 38 mm, or 2.0 mm to 36 mm, 5.0 mm to 33 mm, or 10 mm to 30 mm. In a further aspect, the device has one dimension that is greater than 3 cm, even up to or greater than 10 cm, 20 cm, or even 30 cm.

In a further aspect, described herein is method for preparing a device comprising an agent, comprising

-   -   (a) admixing at least one polymer and at least one agent to         produce an admixture;     -   (b) processing the admixture to produce a device of a desired         shape, wherein the device comprises at least two exposed         surfaces; and     -   (c) contacting the device with a sufficient amount of a fluid         for a sufficient time to change the surface morphology of the         polymer, wherein at least one exposed surface or at least one         part of at least one exposed surface of the device is not         contacted with the fluid, and     -   wherein steps (a) and (b) do not involve the use of a solvent.

In another aspect, described herein is a method for preparing a device comprising an agent, comprising

(a) admixing at least one polymer and at least one agent to produce an admixture;

(b) processing the admixture to produce a device of a desired shape; and

(c) contacting the device with a sufficient amount of a fluid for a sufficient time to change the surface morphology of the polymer,

wherein steps (a) and (b) do not involve the use of a solvent.

In another aspect, described herein is a method for preparing a device comprising an agent, comprising

(a) admixing at least one polymer and at least one agent to produce an admixture;

(b) processing the admixture to produce a device of a desired shape; and

(c) contacting the device with a sufficient amount of a fluid for a sufficient time to change the surface morphology of the polymer,

wherein steps (a) and (b) involves the use of a non-solvent for the polymer.

In a further aspect, described herein is method for preparing a device comprising at least one polymer and at least one agent, comprising contacting the device with the agent incorporated therein with a sufficient amount of a fluid for a sufficient time to change the surface morphology of the polymer.

In another method, described herein is a method for preparing a device comprising at least one polymer and at least one agent, comprising contacting the device with the agent incorporated therein with a sufficient amount of a fluid for a sufficient time to change the surface morphology of the polymer, wherein at least one exposed surface or at least one part of at least one exposed surface of the device is not contacted with the fluid.

In certain aspects, the polymer and agent are admixed to form a blend or admixture. Admixing step (a) can be performed using techniques known in the art. For example, the polymer and agent can be dry blended (i.e., mixing of particulates of the polymer and the agent) using, for example, a Patterson-Kelley V-blender, or granulated prior to processing step (b). It is contemplated that other components such as, for example, excipients, can be admixed with the polymer and the agent prior to processing.

In certain aspects of the methods described herein, the admixing step does not involve the use of a solvent. There are a number of disadvantages associated with the use of a solvent during the admixing of the polymer and the agent. First, the use of a solvent during admixing requires additional processing steps to remove the solvent. Second, if the delivery system is to be implanted into a subject, the selected solvent has to be biocompatible if any residual solvent remains in the device. The solvent can adversely affect the overall morphology of the delivery system, which can lead to undesirable release patterns. The solvent can adversely affect the stability of the bioactive agent during the manufacturing process. Finally, the solvent level requires control, because it has to be low enough to meet regulatory guidelines.

It is contemplated that steps (a) and/or (b) can be performed in batch or continuously. In another aspect, steps (a) and (b) can employ a non-solvent for the polymer. The phrase “non-solvent for a polymer” is defined herein as any component or compound that can facilitate the mixing of the polymer and the agent, wherein the polymer is substantially insoluble in the component or compound. In a further aspect, the non-solvent is any solvent that dissolves less than 5%, less than 4%, less than 3%, less than 2%, less than 1%, less than 0.75%, less than 0.5%, less than 0.25%, or 0% by weight of the polymer. In a further aspect, admixing step (a) involves the use the use of a non-solvent for the polymer in granulating the polymer and the agent.

The processing of the admixture is performed under conditions such that the agent is intimately mixed or dispersed throughout the polymer. The admixture can be processed by a variety of techniques, such as, for example, melt extruding, injection molding, compression molding, or roller compacting the admixture into a desired shape or structure. Compression manufacturing techniques can include, but are not limited to tabletting. Depending upon processing conditions, the polymer used as a starting material in the admixing step may or may not be the same polymer present in the final device. For example, the polymer during processing may undergo polymerization or depolymerization reactions, which ultimately can produce a different polymer that was used prior to processing. Thus, the term “polymer” as used herein covers the polymers used as starting materials as well as the final polymer present in the device produced by the methods described herein.

The device can have various shapes and sizes depending upon the processing technique that is selected. In a further aspect, the device comprises at least two exposed surfaces. The term “exposed surface” as defined herein is any surface of the device that can be contacted with the fluid. For example, when the device is a cylindrical rod, the device has three exposed surfaces (the two ends and the longitudinal surface). In further aspects, the device has one exposed surface, two exposed surfaces, three exposed surfaces, or greater than three exposed surfaces that have not been contacted with the fluid. This allows for greater controllability of the rate and direction of the release of the agent. The exposed polymer surface not being contacted with the fluid includes the aspects of both (a) controlling the fluid so as not to contact at least one surface of the device during the contacting step or (b) by removing a portion of the treated polymer layer of the treated device to thereby expose uncontacted polymer surface. For aspect (b), for a rod, for example, the entire rod can be fluid treated and then the rod end(s) sliced, cut, sheared, chopped off, or removed in some other manner to expose untreated surface.

In further aspects, the exposed surface or surfaces that have not been contacted with the fluid can be just a portion of the surface, i.e., not the entire surface. That is, in certain aspects, it is not necessary to fluid treat the entire polymer surface, thus, partial surface treatment can be acceptable. For example, when the device is a rod, one entire end surface can be free of contact with the fluid or just part of the one end surface can be free of contact with the fluid. In further aspects, the exposed surface or surfaces that have not been contacted with the fluid can be both one or more entire surfaces and one or more partial surfaces. For example, when the device is a rod, the entire first end surface can be free of fluid contact and part of the surface of the second end can be free of fluid contact.

In a further aspect, the device can be a depot or implant. In a further aspect, the device can be in the shape of a rod, a fiber, a cylinder, a bead, a ribbon, a disc, a wafer, a free-formed shaped solid, or a variety of other shaped solids. In a further aspect, the device is not a sphere such as, for example, a microsphere or microparticle. The device can have any regular or irregular shape and can have any cross section like circular, rectangular, triangular, oval, and the like. In a further aspect, the device comprises a rod comprising two ends and a longitudinal surface, wherein the ends of the rod are not contacted with the surface, and wherein the longitudinal surface is contacted with the fluid.

The delivery systems produced herein can also include a coated article. In a further aspect, described herein is a method for producing a coated article, comprising

(a) coating the outer surface of the article with at least one polymer to produce the coated article; and

(b) contacting the coated article with a sufficient amount of a fluid to change the surface morphology of at least part of the surface of the polymer.

In this aspect, depending upon the end-use, an agent can be incorporated in the article prior to coating, the agent can be incorporated in the polymer prior to coating the article, or the agent can be incorporated in the article and the polymer coating. It is contemplated that one or more agents can be incorporated in the article and/or the polymer coating. The term “article” is defined herein as any substrate that is capable of being coated with a polymer. In a further aspect, the article to be coated can be a medical device such as, for example, a stent, suture, surgical clip, rod, pin, anchor, mesh, scaffold, tissue-generating scaffold, medical electronic device, a wound dressing, a membrane, an orthopedic device for delivering an antibiotic or growth factor, a device for a dermal application for delivering an anesthetic or growth factor, and the like.

The coating of the article can be accomplished using techniques known in the art. In a further aspect, the coating can be applied by using a solution or dispersion of the polymer. In this aspect, if the agent is not incorporated into the article prior to coating, the agent can be dissolved or dispersed in the polymer solution. In another aspect, the polymer and, optionally, the agent are melt blended then applied to the outer surface of the article. In another aspect, the polymer and, optionally, the agent are prepared as a powder then powder coated on the article. It is also contemplated that all or a portion of the article can be coated with the polymer or polymer and agent.

For the coated article, typically the entire polymer exposed surfaces are contacted with the fluid. However, similar to the device above, partial contacting, i.e., only a portion of the exposed polymer is contacted with the fluid, can be performed or part of the polymer surface is removed to expose untreated surface.

In a further aspect, once the delivery system (i.e. device or coated article) has been produced, it is contacted with a fluid in order to change the surface properties of the device or coated article and, thus, alter the release properties of the device or coated article. In a further aspect, the device or coated article is contacted with a fluid in a sufficient amount for a sufficient time to change the surface morphology of the polymer. Not wishing to be bound by theory, it is believed that the fluid diffuses into the outer layer (a) to lower the Tg of the polymer or (b) to dissolve and/or gel the polymer, so that the polymer molecules rearrange to produce a smooth or smoother surface coating on the device or coated article. This fluid effect results in changing or altering the surface properties on the device or coated article such as, for example, porosity and permeability, which can ultimately reduce the release of the agent incorporated in the device or the coated article. It is also contemplated that all or a portion of the polymer of the device or coated article can be contacted with the fluid.

The fluid used for the surface treatment can include a single fluid or a mixture of two or more fluids in any ratio. In a further aspect, the fluid can be selected based upon the solubility of the polymer to be used. For example, the fluid can be a mixture of liquids, one of which will solubilize the polymer and the other that does not or both will solubilize the polymer. By selecting the fluid system to be used and the duration of the contacting step, it is possible to change the morphology of the polymer and, ultimately, the release pattern of the device. For example, if slower release of the agent from the device is desired, the device can be contacted with the fluid for longer periods of time in order to change the surface morphology of the device to a greater extent.

In a further aspect, the fluid comprises a liquid. Examples of liquids include, but are not limited to, hydrocarbons, halogenated hydrocarbons, ethers, esters, acids, bases, alcohols, ketones, alkanes, aromatics, and the like. In another aspect, the fluid is methylene chloride, chloroform, acetone, anisole, ethyl acetate, methyl acetate, N-methyl-2-pyrrolidone, hexafluoroisopropanol, tetrahydrofuran, dimethylsulfoxide, water, 2-pyrollidone, triethyl citrate, ethyl lactate, propylene carbonate, benzyl alcohol, benzyl benzoate, Miglyol 810, isopropanol, ethanol, super critical carbon dioxide, acetonitrile, water, or a mixture thereof.

In another aspect, the fluid comprises a gas. Compounds that are gaseous at standard temperature and pressure can be used herein as the fluid. In a further aspect, the gas comprises nitrogen, ethylene oxide, a polyfluorochloro compound, water vapor, a vapor of an organic solvent, or a mixture thereof. The device or coated article can be contacted with the gas at operating conditions, such as ambient, elevated, or reduced temperatures, depending upon the composition of the device or coated article and the gas selected.

The delivery system can be exposed to the fluid once or multiple times. In another aspect, after the contacting step, the fluid can optionally be removed from the delivery system. The amount of fluid that is removed from the delivery system in this aspect can vary, and will depend upon the desired release profile to be achieved. The device or coated article can be contacted with the fluid using techniques known in the art. In a further aspect, when the fluid is a liquid, the device or article can be contacted with the liquid by immersing the device in the liquid or spraying the liquid on the device. In another aspect, during the processing of the polymer/agent admixture, the admixture can be extruded with the fluid. In a further aspect, the polymer/agent admixture can be extruded through a liquid rich dye. In another aspect, the contacting step can be continuous, where a steady stream of fluid is in contact with the device. In other aspects, when the fluid is a liquid, the contacting step can be performed by an annular ring with an aerosol solvent, a pan coating, or by vapor phase equilibration. When the fluid is a gas, in a further aspect, the device or coated article can be contacted with a steady stream of the gas. Alternatively, the device or coated article can be placed in a chamber that is to be filled with the gas. In further aspects, an entire exposed surface or a portion of the exposed surface of the polymer of the delivery systems (devices and coated articles) can be fluid treated. That is, it is not necessary in certain aspects to treat the entire polymer surface.

The time of the fluid exposure can vary depending upon the fluid and polymer selected and the desired release pattern to be achieved. The contacting step can range from greater than zero, such as just over a second, to minutes, to hours, or to several days. In various aspects, the contacting time is from 0.1 seconds to one hour, 0.5 seconds to 30 minutes, one second to 10 minutes, two seconds to 5 minutes, three seconds to 60 seconds, or five seconds to 30 seconds. In another aspect, the contacting time is from one second to 10 seconds or one second to five seconds. In further aspects, different fluids or different mixtures of fluids can be used during a series of fluid exposures.

Other process conditions can include, but are not limited to, temperature and pressure. In a further aspect, when the fluid is a liquid, the temperature of the contacting step is less than the boiling point of the liquid. In another aspect, the temperature of the contacting step is less than the melting point of the polymer. In another aspect, when the fluid is a gas, the pressure of the contacting step can be at atmospheric pressure or greater than atmospheric pressure.

Typically, after the contacting step the delivery system is dried to remove some or all of the fluid. In a further aspect, after the contacting step, the delivery system is washed with water.

In a further aspect, the device is prepared by dry blending a bioactive agent with a poly(lactide-co-glycolide) polymer (PLG) such as, for example, 85:15 PLG. In a further aspect, when the delivery system is a device, the device is prepared by dry blending poly(lactide-co-glycolide), poly(lactide), or a combination thereof, with a bioactive agent to produce an admixture, melt extruding the admixture to produce a rod, contacting the rod with ethyl acetate, and cutting the rod into one or more smaller rods having a predetermined length. In this aspect, the two ends of the cut up rods have not been contacted with the fluid. Thus, the surface morphology of the ends of the rod is different when compared to longitudinal surface of the rod.

A variety of agents can be used in the methods described herein. As used herein, in reference to the invention, “agent” includes both a bioactive agent or a non-bioactive agent.

In a further aspect, the agent is a bioactive agent. The term “bioactive agent” (i.e., biologically active agent, drug, or medicament) as used herein includes without limitation physiologically or pharmacologically active substances that act locally or systemically in the body. A biologically active agent is a substance used for the treatment, prevention, diagnosis, cure or mitigation of disease or illness, a substance which affects the structure or function of the body, or pro-drugs, which become biologically active or more active after they have been placed in a predetermined physiological environment. Bioactive agents include biologically, physiologically, or pharmacologically active substances that act locally or systemically in the human or animal body. Various forms of the medicaments or biologically active materials can be used, which are capable of being released from the solid matrix into adjacent tissues or fluids. A liquid or solid bioactive agent can be incorporated in the delivery systems described herein. The bioactive agents are at least very slightly water soluble, preferably moderately water soluble, and are diffusible through the polymeric composition. They can be acidic, basic, or amphoteric salts. They can be nonionic molecules, polar molecules, or molecular complexes capable of hydrogen bonding. The biologically-active agent may be included in the compositions in the form of, for example, an uncharged molecule, a molecular complex, a salt, an ether, an ester, an amide, polymer drug conjugate, or other form to provide the effective biological or physiological activity. Examples of bioactive agents that incorporated into systems herein include, but are not limited to, peptides, proteins such as hormones, enzymes, antibodies and the like, nucleic acids such as aptamers, iRNA, DNA, RNA, antisense nucleic acid or the like, antisense nucleic acid analogs or the like, low-molecular weight compounds, or high-molecular-weight compounds. Bioactive agents contemplated for use in the delivery systems include anabolic agents, antacids, anti-asthmatic agents, anti-cholesterolemic and anti-lipid agents, anti-coagulants, anti-convulsants, anti-diarrheals, anti-emetics, anti-infective agents including antibacterial and antimicrobial agents, anti-inflammatory agents, anti-manic agents, antimetabolite agents, anti-nauseants, anti-neoplastic agents, anti-obesity agents, anti-pyretic and analgesic agents, anti-spasmodic agents, anti-thrombotic agents, anti-tussive agents, anti-uricemic agents, anti-anginal agents, antihistamines, appetite suppressants, biologicals, cerebral dilators, coronary dilators, bronchiodilators, cytotoxic agents, decongestants, diuretics, diagnostic agents, erythropoietic agents, expectorants, gastrointestinal sedatives, hyperglycemic agents, hypnotics, hypoglycemic agents, immunomodulating agents, ion exchange resins, laxatives, mineral supplements, mucolytic agents, neuromuscular drugs, peripheral vasodilators, psychotropics, sedatives, stimulants, thyroid and anti-thyroid agents, tissue growth agents, uterine relaxants, vitamins, or antigenic materials. Other bioactive agents include androgen inhibitors, polysaccharides, growth factors, hormones, anti-angiogenesis factors, dextromethorphan, dextromethorphan hydrobromide, noscapine, carbetapentane citrate, chlophedianol hydrochloride, chlorpheniramine maleate, phenindamine tartrate, pyrilamine maleate, doxylamine succinate, phenyltoloxamine citrate, phenylephrine hydrochloride, phenylpropanolamine hydrochloride, pseudoephedrine hydrochloride, ephedrine, codeine phosphate, codeine sulfate morphine, mineral supplements, cholestryramine, N-acetylprocainamide, acetaminophen, aspirin, ibuprofen, phenyl propanolamine hydrochloride, caffeine, guaifenesin, aluminum hydroxide, magnesium hydroxide, peptides, polypeptides, proteins, amino acids, hormones, interferons, cytokines, and vaccines. Representative drugs or bioactive materials that can be used in the polymer system or solid matrix of the present invention include, but are not limited to, peptide drugs, protein drugs, desensitizing materials, antigens, anti-infective agents such as antibiotics, antimicrobial agents, antiviral, antibacterial, antiparasitic, antifungal substances and combination thereof, antiallergenics, androgenic steroids, decongestants, hypnotics, steroidal anti-inflammatory agents, anti-cholinergics, sympathomimetics, sedatives, miotics, psychic energizers, tranquilizers, vaccines, estrogens, progestational agents, humoral agents, prostaglandins, analgesics, antispasmodics, antimalarials, antihistamines, cardioactive agents, nonsteroidal anti-inflammatory agents, antiparkinsonian agents, antihypertensive agents, β-adrenergic blocking agents, nutritional agents, and the benzophenanthridine alkaloids. The agent may further be a substance capable of acting as a stimulant, sedative, hypnotic, analgesic, anticonvulsant, and the like. The delivery system can contain a large number of bioactive active agents either singly or in combination. Other bioactive agents include but are not limited to analgesics such as acetaminophen, acetylsalicylic acid, and the like; anesthetics such as lidocaine, xylocalne, and the like; anorexics such as dexadrine, phendimetrazine tartrate, and the like; antiarthritics such as methylprednisolone, ibuprofen, and the like; antiasthmatics such as terbutaline sulfate, theophylline, ephedrine, and the like; antibiotics such as sulfisoxazole, penicillin G, ampicillin, cephalosporins, amikacin, gentamicin, tetracyclines, chloramphenicol, erythromycin, clindamycin, isoniazid, rifampin, and the like; antifungals such as amphotericin B, nystatin, ketoconazole, and the like; antivirals such as acyclovir, amantadine, and the like; anticancer agents such as cyclophosphamide, methotrexate, etretinate, and the like; anticoagulants such as heparin, warfarin, and the like; anticonvulsants such as phenyloin sodium, diazepam, and the like; antidepressants such as isocarboxazid, amoxapine, and the like; antihistamines such as diphenhydramine HCl, chlorpheniramine maleate, and the like; hormones such as insulin, progestins, estrogens, corticoids, glucocorticoids, androgens, and the like; tranquilizers such as thorazine, diazepam, chlorpromazine HCl, reserpine, chlordiazepoxide HCl, and the like; antispasmodics such as belladonna alkaloids, dicyclomine hydrochloride, and the like; vitamins and minerals such as essential amino acids, calcium, iron, potassium, zinc, vitamin B₁₂, and the like; cardiovascular agents such as prazosin HCl, nitroglycerin, propranolol HCl, hydralazine HCl, pancrelipase, succinic acid dehydrogenase, and the like; peptides and proteins such as LHRH, somatostatin, calcitonin, growth hormone, glucagon-like peptides, growth releasing factor, angiotensin, FSH, EGF, bone morphogenic protein (BMP), erythopoeitin (EPO), interferon, interleukin, collagen, fibrinogen, insulin, Factor VIII, Factor IX, Enbrel®, Rituxam®, Herceptin®, alpha-glucosidase, Cerazyme/Ceredose®, vasopressin, ACTH, human serum albumin, gamma globulin, structural proteins, blood product proteins, complex proteins, enzymes, antibodies, monoclonal antibodies, and the like; prostaglandins; nucleic acids; carbohydrates; fats; narcotics such as morphine, codeine, and the like, psychotherapeutics; anti-malarials, L-dopa, diuretics such as furosemide, spironolactone, and the like; antiulcer drugs such as rantidine HCl, cimetidine HCl, and the like.

Immunological agents that can be used herein include, cytokines, interleukins, interferon, colony stimulating factor, tumor necrosis factor, and the like; allergens such as cat dander, birch pollen, house dust mite, grass pollen, and the like; antigens of cush bacterial organisms as Streptococcus pneumoniae, Haemophilus influenzae, Staphylococcus aureus, Streptococcus pyrogenes, Corynebacterium diphteriae, Listeria monocytogenes, Bacillus anthracis, Clostridium tetani, Clostridium botulinum, Clostridium perfringens. Neisseria meningitides, Neisseria gonorrhoeae, Streptococcus mutans. Pseudomonas aeruginosa, Salmonella typhi, Haemophilus parainfluenzae, Bordetella pertussis, Francisella tularensis, Yersinia pestis, Vibrio cholerae, Legionella pneumophila, Mycobacterium tuberculosis, Mycobacterium leprae, Treponema pallidum, Leptspirosis interrogans, Borrelia burgddorferi, Campylobacter jejuni, and the like; antigens of such viruses as smallpox, influenza A and B, respiratory synctial, parainfluenza, measles, HIV, SARS, varicella-zoster, herpes simplex 1 and 2, cytomeglavirus, Epstein-Barr, rotavirus, rhinovirus, adenovirus, papillomavirus, poliovirus, mumps, rabies, rubella, coxsackieviruses, equine encephalitis, Japanese encephalitis, yellow fever, Rift Valley fever, lymphocytic choriomeningitis, hepatitis B, and the like; antigens of such fungal, protozoan, and parasitic organisms such as Cryptococcuc neoformans, Histoplasma capsulatum, Candida albicans, Candida tropicalis, Nocardia asteroids, Rickettsia ricketsii, Rickettsia typhi, Mycoplasma pneumoniae, Chlamyda psittaci, Chlamydia trachomatis, Plasmodium falciparum, Trypanasoma brucei, Entamoeba histolytica, Toxoplasma gondii, Trichomonas vaginalis, Schistosoma mansoni, and the like. These antigens may be in the form of whole killed organisms, peptides, proteins, glycoproteins, carbohydrates, or combinations thereof.

In a specific aspect, the bioactive agent comprises a drug, an immunological agent, an antigen, a protein, a peptide, an oligonucleotide, or a mixture thereof.

Although there are numerous applications for bioactive agents, the devices and coated articles produced herein are useful in releasing non-bioactive agents as well. Examples of non-bioactive agents include, but are not limited to, an adhesive, a pesticide, a fragrance, an antifoulant, a dye, a salt, an oil, an ink, a cosmetic, a catalyst, a detergent, a curing agent, a flavor, a fuel, a herbicide, a metal, a paint, a photographic agent, a biocide, a pigment, a plasticizer, a propellant, a stabilizer, a polymer additive, or any combination thereof.

The polymers useful herein are biocompatible and either biodegradable or non-biodegradable. In a further aspect, polymers useful in the methods described herein include, but are not limited to, a silicone, a poly(diene) such as poly(butadiene) and the like; a poly(alkene) such as polyethylene, polypropylene, and the like; a poly(acrylic) such as poly(acrylic acid) and the like; a poly(methacrylic) such as poly(methyl methacrylate) or a poly(hydroxyethyl methacrylate), and the like; a poly(vinyl ether); a poly(vinyl alcohol); a poly(vinyl ketone); a poly(vinyl halide) such as poly(vinyl chloride) and the like; a poly(vinyl nitrile), a poly(vinyl ester) such as poly(vinyl acetate) and the like; a poly(vinyl pyridine) such as poly(2-vinyl pyridine) or poly(5-methyl-2-vinyl pyridine) and the like; a poly(styrene); a poly(carbonate); a poly(ester); a poly(orthoester) including a copolymer; a poly(esteramide); a poly(anhydride); a poly(urethane); a poly(amide); a cellulose ether such as methyl cellulose, hydroxyethyl cellulose, hydroxypropyl methyl cellulose, and the like; a cellulose ester such as cellulose acetate, cellulose acetate phthalate, cellulose acetate butyrate, and the like; a poly(saccharide), a protein, gelatin, starch, gum, a resin, and the like. These materials may be used alone, as physical mixtures (blends), combinations, or as copolymers. Derivatives of any of the polymers listed above can also be used.

In a specific aspect, the polymer comprises a silicone, a poly(diene), a poly(alkene), a poly(acrylic), a poly(methacrylic), poly(vinyl ether), a poly(vinyl alcohol), a poly(vinyl ketone), a poly(vinyl halide), a poly(vinyl nitrile), a poly(vinyl ester), a poly(vinyl pyridine), a poly(styrene), a poly(carbonate), a poly(ester), a poly(orthoester), a poly(esteramide), a poly(anhydride), a poly(urethane), a poly(amide), a cellulose ether, a cellulose ester, a poly(saccharide), a protein, gelatin, starch, a gum, a resin, or any combination, blend, or copolymer thereof.

In a further aspect, the polymer of the device or coated article includes a biocompatible, non-biodegradable polymer such as, for example, a polyacrylate; a polymer of ethylene-vinyl acetate; an acyl substituted cellulose acetate; a non-degradable polyurethane; a polystyrene; a polyvinyl chloride; a polyvinyl fluoride; a poly(vinyl imidazole); a chlorosulphonate polyolefin; a polyethylene oxide; or a blend, combination, or copolymer thereof.

In another aspect, the polymer of the device or coated article includes a biocompatible, biodegradable polymer such as, but limited to, a poly(lactide), a poly(glycolide), a poly(lactide-co-glycolide), a poly(lactic acid), a poly(glycolic acid), a poly(lactic acid-co-glycolic acid), a poly(caprolactone), a poly(orthoester), a poly(phosphazene), a poly(hydroxybutyrate) or a copolymer containing a poly(hydroxybutarate); a poly(lactide-co-caprolactone); a polycarbonate; a polyesteramide; a polyanhydride; a poly(dioxanone), a poly(alkylene alkylate); a copolymer of polyethylene glycol and a polyorthoester, a biodegradable polyurethane, a poly(amino acid), a polyamide, a polyesteramide, a polyetherester, a polyacetal, a polycyanoacrylate, a poly(oxyethylene)/poly(oxypropylene) copolymer, polyacetals, polyketals, polyphosphoesters, polyhydroxyvalerates or a copolymer containing a polyhydroxyvalerate, polyalkylene oxalates, polyalkylene succinates, poly(maleic acid), and copolymers, terpolymers, combinations, or blends thereof.

In another aspect, the polymer comprises a biodegradable polymer, wherein the biodegradable polymer comprises a poly(caprolactone), a poly(orthoester), a poly(phosphazene), a poly(hydroxybutyrate) or a copolymer containing poly(hydroxybutarate), a poly(lactide-co-caprolactone), a polycarbonate, a polyesteramide, a polyanhydride, a poly(dioxanone), a poly(alkylene alkylate), a copolymer of polyethylene glycol and polyorthoester, a biodegradable polyurethane, a poly(amino acid), a polyetherester, a polyacetal, a polycyanoacrylate, poly(oxyethylene)/poly(oxypropylene) copolymer, or a combination, blend, or copolymer thereof.

In a further aspect, the device is an implant or rod comprising a biodegradable polymer, wherein the bioactive agent is imbedded within the implant. In a further aspect, the bioactive agent is encapsulated in an implant or rod composed of poly(lactide-co-glycolide), poly(lactide), poly(glycolide), or a mixture thereof. Lactide/glycolide polymers for drug-delivery formulations are typically made by melt polymerization through the ring opening of lactide and glycolide monomers. Some polymers are available with or without carboxylic acid end groups. When the end group of the poly(lactide-co-glycolide), poly(lactide), or poly(glycolide) is not a carboxylic acid, for example, an ester, then the resultant polymer is referred to herein as blocked or capped. The unblocked polymer, conversely, has a terminal carboxylic group. The biodegradable polymers herein can be blocked or unblocked. In a further aspect, linear lactide/glycolide polymers are used; however star polymers can be used as well. In certain aspects, high molecular weight polymers can be used for medical devices, for example, to meet strength requirements. In other aspects, low or medium molecular weight polymers can be used for drug-delivery and vaccine delivery products where resorption time of the polymer and not material strength is as important. The lactide portion of the polymer has an asymmetric carbon. Commercially racemic DL-, L-, and D-polymers are available. The L-polymers are more crystalline and resorb slower than DL-polymers. In addition to copolymers comprising glycolide and DL-lactide or L-lactide, copolymers of L-lactide and DL-lactide are available. Additionally, homopolymers of lactide or glycolide are available.

In the case when the biodegradable polymer is poly(lactide-co-glycolide), poly(lactide), or poly(glycolide), the amount of lactide and glycolide in the polymer can vary. In a further aspect, the biodegradable polymer contains 0 to 100 mole %, 40 to 100 mole %, 50 to 100 mole %, 60 to 100 mole %, 70 to 100 mole %, or 80 to 100 mole % lactide and from 0 to 100 mole %, 0 to 60 mole %, 10 to 40 mole %, 20 to 40 mole %, or 30 to 40 mole % glycolide, wherein the amount of lactide and glycolide is 100 mole %. In a further aspect, the biodegradable polymer can be poly(lactide), 95:5 poly(lactide-co-glycolide) 85:15 poly(lactide-co-glycolide), 75:25 poly(lactide-co-glycolide), 65:35 poly(lactide-co-glycolide), or 50:50 poly(lactide-co-glycolide) where the ratios are mole ratios.

Polymers that are useful for the present invention are those having an intrinsic viscosity of from 0.15 to 2.0, 0.15 to 1.5 dL/g, 0.25 to 1.5 dL/g, 0.25 to 1.0 dL/g, 0.25 to 0.8 dL/g, 0.25 to 0.6 dL/g, or 0.25 to 0.4 dL/g as measured in chloroform at a concentration of 0.5 g/dL at 30° C. In a further aspect, when the biodegradable polymer is poly(lactide-co-glycolide), poly(lactide), or poly(glycolide), the polymer has an intrinsic viscosity of from 0.15 to 2.0, 0.15 to 1.5 dL/g, 0.25 to 1.5 dL/g, 0.25 to 1.0 dL/g, 0.25 to 0.8 dL/g, 0.25 to 0.6 dL/g, or 0.25 to 0.4 dL/g as measured in chloroform at a concentration of 0.5 g/dL at 30° C.

When the device or coated article is used to deliver a bioactive agent, other pharmaceutically-acceptable components can be incorporated in the delivery system in combination with the bioactive agent. For example, the pharmaceutically-acceptable component can include, but is not limited to, a fatty acid, a sugar, a salt, a water-soluble polymer such as polyethylene glycol, a protein, polysaccharide, or carboxmethyl cellulose, a surfactant, a plasticizer, a high- or low-molecular-weight porosigen such as polymer or a salt or sugar, or a hydrophobic low-molecular-weight compound such as cholesterol or a wax.

In further aspects of the invention, the invention includes devices and coated articles made by the methods described herein.

In a further aspect, described herein are devices comprising at least one polymer and at least one agent, wherein the agent is dispersed in the polymer, wherein the device comprises at least two exposed surfaces of the same polymer, wherein at least one of the exposed surfaces or at least one part of at least one exposed surface has surface morphology different than the other exposed surface or surfaces. The device can be composed of one polymer or a mixture of two or more polymers. Regardless if one or more polymers are used, the polymer or polymers are evenly distributed throughout the device. Thus, in various aspects, when two or more polymers are used to produce the device, the polymers are not two distinct polymer phases (e.g., co-extrusion of two polymers) but a mixture of the polymers.

Using the techniques described herein, it is possible to change the surface morphology of one or more exposed surfaces of the delivery system so that the delivery system has varying (i.e., different) surface morphologies. This is desirable for a number of different applications. For example, when the delivery system is a rod used as an implant, wherein the ends of the rod are not contacted with a fluid but the longitudinal surface is contacted with the fluid, the longitudinal surface has a surface morphology that is different than that of the ends of the rod. In this aspect, the rate of release and the direction of release can be better controlled. The delivery systems produced by the methods described herein also have the added benefit of containing more of the agent (i.e., higher loading). In a further aspect, the agent is greater than 30%, greater than 40%, or greater than 50% by weight of the device or coating on the coated article. In the case when the delivery system is to be implanted into a subject, the greater loading capacity results in higher doses of the agent that can released over a longer period of time as well as the use of smaller implants.

In another aspect, described herein is a polymer coated article that has been treated with a fluid of this invention. In a specific aspect, the article comprises at least one first exposed surface and a polymer coating comprising a second exposed surface, wherein the polymer coating is connected to the first exposed surface of the article, wherein the morphology near the second exposed surface of at least part of the polymer coating is different than the morphology of the remaining polymer coating. The term “connected” as used herein includes when the polymer is adjacent to (i.e., intimate contact with) the article or is indirectly attached to the article by way of one or more intermediate layers. As described above, the agent can be present in the article prior to the application of the polymer coating, the agent can be incorporated into the polymer prior to coating, or a combination thereof. The morphology near the second exposed surface of at least part of the polymer coating is different than the morphology of the remaining polymer coating. The term “near” is defined herein to include the exposed surface of the polymer coating and a predetermined distance below the exposed surface of the coating. The distance below the surface can vary and will depend upon the selection of the fluid, the contacting time with the fluid, and the desired release pattern. At least part of or the entire polymer surface can be fluid treated, and thus have a different morphology than the underlying polymer surface.

EXAMPLES

The following examples are put forth so as to provide those of ordinary skill in the art with a complete disclosure and description of how the compounds, compositions, and methods described and claimed herein are made and evaluated, and are intended to be purely exemplary and are not intended to limit the scope of what the inventors regard as their invention. Efforts have been made to ensure accuracy with respect to numbers (e.g., amounts, temperature, etc.) but some errors and deviations should be accounted for. Unless indicated otherwise, parts are parts by weight, temperature is in degrees Centigrade (° C.) or is at ambient temperature, and pressure is at or near atmospheric. There are numerous variations and combinations of reaction conditions, e.g., component concentrations, component mixtures, desired solvents, solvent mixtures, temperatures, pressures and other reaction ranges and conditions that can be used to optimize the product purity and yield obtained from the described process. Only reasonable and routine experimentation will be required to optimize such process conditions.

Example 1 Fabrication of Implants Containing 45 Wt % Vitamin B₁₂

An implant formulation was made with vitamin B₁₂ and poly(DL-lactide). The poly(DL-lactide) was ester capped and had an inherent viscosity of 0.37 dL/g. The inherent viscosity was measured at 30° C. with 0.5 gm/dL polymer concentration in chloroform.

The desired vitamin B₁₂ content in the implant was 45 wt % vitamin B₁₂. First vitamin B₁₂ (2.25 gm) and the poly(DL-lactide) (2.75 gm) were dry blended using a mortar and pestle to form a blended powder. Next a Tinius Olsen Model UE-4-78 melt plastometer was used to extrude the blended powder. The Tinius Olsen is a solid block of steel about 80 mm in diameter and about 160 mm high/long with a hollow core about 13 mm in diameter. The discharge of the core has a shoulder that allows different size “dies” to be used based on the desired diameter of extruded rod. For this run, a 1.5-mm die was used, meaning that the core of the die was 1.5 mm in diameter. The main block of the Tinius Olsen has heater bands encased by insulation and a shroud that allow the Tinius Olsen to be heated to a desired temperature. A thermocouple was used to measure the temperature of the block. The control system then uses the thermocouple values to either turn the heater bands on or off. Throughout the extrusion process, the heater bands will switch off and on to maintain the desired temperature. The blend, approximately 5 gm, was loaded into the Tinius Olsen which had been equilibrated to 90° C. A charging rod was placed in the core of the Tinius Olsen to compress the blend and a weight of 3.7 kg was placed on the end of the charging rod to aid in the compaction of the blend. The equilibration time for the blend to melt lasted for about 15 minutes. After an extrusion load of 10,400 gm was placed on the charging rod, the plug was removed from the discharge area to begin the extrusion run. The 5-gm charge afforded 5 segments of extruded rod each having a length of about 20 cm.

Next ethyl acetate was placed in a graduated cylinder and one end of the rod was held with forceps and dipped in the ethyl acetate for about 5 seconds. The implants were then dried at ambient temperature. Once the implants were dry, the ends of the extruded rod segments were cut and discarded. The remaining treated segment was cut into implants that had the cylindrical portion treated with ethyl acetate and the ends left untreated. The only treated part was thus that portion of the implant that came into contact with the cylindrical wall of the implant. The vitamin B₁₂ content was 45 wt %. The in vitro release characteristics of the vitamin B₁₂ implants made with poly(DL-lactide) by the above-described manufacturing process (with and without ethyl acetate exposure) are shown in FIG. 1. These release data showed that the ethyl acetate treated implants released vitamin B₁₂ with less burst of vitamin B₁₂ and at a slower rate of release as compared to implants not treated with ethyl acetate.

Example 2 Fabrication of Implants Containing 30 wt % of Leuprolide a 9-Amino-Acid Peptide (PROPHETIC)

An implant formulation can be made with small peptides (3 to 12 amino acids) or large peptides (13 to 50 amino acids) with poly(DL-lactide) or poly(lactide-co-glycolide).

Leuprolide is a 9-amino-acid peptide that is an LHRH agonist indicated for the treatment of prostate cancer. The desired leuprolide content in the implant is 35 wt % peptide. To prepare a depot formulation of luprolide, leuprolide and poly(DL-lactide) or poly(lactide-co-glycolide) can be dry blended in a variety of ways including the use of a mortar and pestle to form a blended powder. Next this blend or admixture is added to a twin-screw extruder having a 2-mm die. An extruded rod of is then made. The rod is subsequently cut to form implants. Each implant is dipped in ethyl acetate for about one time for about 5 seconds. The implants are then dried at ambient temperature.

Example 3 Fabrication of Implants Containing 10 wt % of Octreotide a 14-Amino-Acid Peptide (PROPHETIC)

An implant formulation can be made with small peptides (3 to 12 amino acids) or large peptides (13 to 50 amino acids) with poly(DL-lactide) or poly(lactide-co-glycolide).

Octreotide is a 14-amino-acid peptide indicated for the treatment of agromegaly. The desired octreotide content in the implant is 10 wt % peptide. To prepare a depot formulation of octreotide, octreotide and poly(DL-lactide) or poly(lactide-co-glycolide) can be dry blended in a variety of ways including the use of a mortar/pestle or by mixing preformed polymer and peptide particles in a V-blender to form a blended powder. Next this blend or admixture is added to a twin-screw extruder having a 2-mm die. An extruded rod of is then made. The rod is subsequently cut to form implants. Each implant is dipped in ethyl acetate for about one time for about 5 seconds or can be dipped for 2 seconds for three times. The implants are then dried at ambient temperature.

Example 4 Fabrication of Implants Containing 44 wt % Deslorelin

An implant formulation was made with Deslorelin and poly(DL-lactide). The poly(DL-lactide) was ester capped and had an inherent viscosity of 0.37 dL/g. The inherent viscosity was measured at 30° C. with 0.5 gm/dL polymer concentration in chloroform.

The desired Deslorelin content in the implant was 44 wt % Deslorelin. First Deslorelin (1.6 gm) and the poly(DL-lactide) (1.6 gm) were dry blended using a mortar and pestle to form a blended powder. Next a Tinius Olsen Model UE-4-78 melt plastometer was used to extrude the blended powder. The Tinius Olsen is a solid block of steel about 80 mm in diameter and about 160 mm high/long with a hollow core about 13 mm in diameter. The discharge of the core has a shoulder that allows different size “dies” to be used based on the desired diameter of extruded rod. For this run, a 3.9-mm die was used, meaning that the core of the die was 3.9 mm in diameter. The main block of the Tinius Olsen has heater bands encased by insulation and a shroud that allow the Tinius Olsen to be heated to a desired temperature. A thermocouple was used to measure the temperature of the block. The control system then uses the thermocouple values to either turn the heater bands on or off. Throughout the extrusion process, the heater bands will switch off and on to maintain the desired temperature. The blend, approximately 3.2 gm, was loaded into the Tinius Olsen which had been equilibrated to 90° C. A charging rod was placed in the core of the Tinius Olsen to compress the blend and a weight of 6.6 kg was placed on the end of the charging rod to aid in the compaction of the blend. The equilibration time for the blend to melt lasted for about 15 minutes. After an extrusion load of 10,400 gm was placed on the charging rod, the plug was removed from the discharge area to begin the extrusion run. The 3.2-gm charge afforded 3 segments of extruded rod each having a length of about 20 cm.

The batch was then segregated into four sections. The first section was not surface treated. The second was treated with ethyl acetate. The third was treated with methylene chloride. The fourth was treated with acetone.

The second section was cut into implants approximately 4 mm in length. The entire implant was then surface treated with ethyl acetate by first mounting the implant on a needle and then dipping into a vial of ethyl acetate. Rod sections three and four were likewise handled, treating their respective surfaces with methylene chloride and acetone. The implants were then dried at ambient temperature. The Deslorelin content was 44 wt %. The in vitro release characteristics of the Deslorelin implants made with poly(DL-lactide) by the above-described manufacturing process (with and without solvent exposure) are shown in FIG. 2. These release data showed that the solvent treated implants released Deslorelin with less burst of Deslorelin (10-33% of the non-treated formulation) and at a slower rate of release as compared to implants not treated with solvent.

Example 5 Fabrication of Implants Containing 50 wt % Risperidone

An implant formulation was made with Risperidone and poly(DL-lactide). The poly(DL-lactide) was ester capped and had an inherent viscosity of 0.37 dL/g. The inherent viscosity was measured at 30° C. with 0.5 gm/dL polymer concentration in chloroform.

The desired Risperidone content in the implant was 50 wt % Risperidone. First Risperidone (2.0 gm) and the poly(DL-lactide) (2.0 gm) were dry blended using a mortar and pestle to form a blended powder. Next a Tinius Olsen Model UE-4-78 melt plastometer was used to extrude the blended powder. The Tinius Olsen is a solid block of steel about 80 mm in diameter and about 160 mm high/long with a hollow core about 13 mm in diameter. The discharge of the core has a shoulder that allows different size “dies” to be used based on the desired diameter of extruded rod. For this run, a 3.9-mm die was used, meaning that the core of the die was 3.9 mm in diameter. The main block of the Tinius Olsen has heater bands encased by insulation and a shroud that allow the Tinius Olsen to be heated to a desired temperature. A thermocouple was used to measure the temperature of the block. The control system then uses the thermocouple values to either turn the heater bands on or off. Throughout the extrusion process, the heater bands will switch off and on to maintain the desired temperature. The blend, approximately 4 grams, was loaded into the Tinius Olsen which had been equilibrated to 90° C. A charging rod was placed in the core of the Tinius Olsen to compress the blend and a weight of 6.6 kg was placed on the end of the charging rod to aid in the compaction of the blend. The equilibration time for the blend to melt lasted for about 20 minutes. After an extrusion load of 10,400 grams was placed on the charging rod, the plug was removed from the discharge area to begin the extrusion run. The 3.2-gm charge afforded 4 segments of extruded rod each having a length of about 20 cm.

The batch was then segregated into three sections. The first section was not surface treated. The second was treated with ethyl acetate. The third was treated with ethanol.

The second section was cut into implants approximately 4 mm in length. The entire implant was then surface treated with ethyl acetate by first mounting the implant on a needle and then dipping into a vial of ethyl acetate. The third rod section was likewise handled, with its surface treated with ethanol. The implants were then dried at ambient temperature. The Risperidone content was 50 wt %. The in vitro release characteristics of the Risperidone implants made with poly(DL-lactide) by the above-described manufacturing process (with and without solvent exposure) are shown in FIG. 3. These release data showed that the solvent treated implants released Risperidone with less burst of Risperidone (<30% of the non-treated formulation for ethyl acetate) and at a slower rate of release as compared to implants not treated with solvent. In particular the reduction of cumulative release in implants treated with ethanol increased over time from a less than 8% reduction at burst to a greater than 14% reduction at Day 14.

Example 6 Fabrication of Implants Containing 50 wt % Vitamin B₁₂

An implant formulation was made with vitamin B₁₂ and poly(DL-lactide). The poly(DL-lactide) was ester capped and had an inherent viscosity of 0.37 dL/g. The inherent viscosity was measured at 30° C. with 0.5 gm/dL polymer concentration in chloroform.

The desired vitamin B₁₂ content in the implant was 50 wt % vitamin B₁₂. First vitamin B₁₂ (2 gm) and the poly(DL-lactide) (2 gm) were dry blended using a mortar and pestle to form a blended powder. Next a Tinius Olsen Model UE-4-78 melt plastometer was used to extrude the blended powder. The Tinius Olsen is a solid block of steel about 80 mm in diameter and about 160 mm high/long with a hollow core about 13 mm in diameter. The discharge of the core has a shoulder that allows different size “dies” to be used based on the desired diameter of extruded rod. For this run, a 3.9-mm die was used, meaning that the core of the die was 3.9 mm in diameter. The main block of the Tinius Olsen has heater bands encased by insulation and a shroud that allow the Tinius Olsen to be heated to a desired temperature. A thermocouple was used to measure the temperature of the block. The control system then uses the thermocouple values to either turn the heater bands on or off. Throughout the extrusion process, the heater bands will switch off and on to maintain the desired temperature. The blend, approximately 4 grams, was loaded into the Tinius Olsen which had been equilibrated to 90° C. A charging rod was placed in the core of the Tinius Olsen to compress the blend and a weight of 6.6 kg was placed on the end of the charging rod to aid in the compaction of the blend. The equilibration time for the blend to melt lasted for about 20 minutes. After an extrusion load of 15,245 gm was placed on the charging rod, the plug was removed from the discharge area to begin the extrusion run. The 4-gm charge afforded 4 segments of extruded rod each having a length of about 20 cm.

The batch was then segregated into four sections. The first section was not surface treated. The second was treated with ethyl acetate. The third was treated with methylene chloride. The fourth was treated with acetone.

The second section was cut into implants approximately 4 mm in length. The entire implant was then surface treated with ethyl acetate by first mounting the implant on a needle and then dipping into a vial of ethyl acetate. Rod sections three and four were likewise handled, treating their respective surfaces with methylene chloride and acetone. The implants were then dried at ambient temperature. The vitamin B₁₂ content was 50 wt %. The in vitro release characteristics of the vitamin B₁₂ implants made with poly(DL-lactide) by the above-described manufacturing process (with and without solvent exposure) are shown in FIG. 4. The release data clearly shows a marked reduction of the burst associated with the non-treated implants when using any of the three solvents. The smallest burst reduction is 42.6% and the largest is 54.1%. The most dramatic results are seen in this formulation with the use of acetone as the solvent.

Example 7 Fabrication of Implants Containing 45 wt % Vitamin B₁₂

An implant formulation was made with vitamin B₁₂ and EVA (ethyl vinyl acetate). The desired vitamin B₁₂ content in the implant was 45 wt % vitamin B₁₂. First vitamin B₁₂ (2 gm) and the EVA (2 gm) were dry blended using a mortar and pestle to form a blended powder. Next a Tinius Olsen Model UE-4-78 melt plastometer was used to extrude the blended powder. The Tinius Olsen is a solid block of steel about 80 mm in diameter and about 160 mm high/long with a hollow core about 13 mm in diameter. The discharge of the core has a shoulder that allows different size “dies” to be used based on the desired diameter of extruded rod. For this run, a 3.9-mm die was used, meaning that the core of the die was 3.9 mm in diameter. The main block of the Tinius Olsen has heater bands encased by insulation and a shroud that allow the Tinius Olsen to be heated to a desired temperature. A thermocouple was used to measure the temperature of the block. The control system then uses the thermocouple values to either turn the heater bands on or off. Throughout the extrusion process, the heater bands will switch off and on to maintain the desired temperature. The blend, approximately 4 grams, was loaded into the Tinius Olsen which had been equilibrated to 90° C. A charging rod was placed in the core of the Tinius Olsen to compress the blend and a weight of 6.6 kg was placed on the end of the charging rod to aid in the compaction of the blend. The equilibration time for the blend to melt lasted for about 20 minutes. After an extrusion load of 15,245 grams was placed on the charging rod, the plug was removed from the discharge area to begin the extrusion run. The 4-gm charge afforded 4 segments of extruded rod each having a length of about 20 cm.

The batch was then segregated into three sections. The first section was not surface treated. The second was treated with methylene chloride for 10 seconds. The third was treated with methylene chloride for 60 seconds.

The second section was cut into implants approximately 4 mm in length. The entire implant was then surface treated with methylene chloride by first mounting the implant on a needle and then dipping into a vial of methylene chloride for 10 seconds. Rod section three was likewise handled, treating the surface with methylene chloride for 60 seconds. The implants were then dried at ambient temperature. The vitamin B₁₂ content was 45 wt %. The in vitro release characteristics of the vitamin B₁₂ implants made with EVA by the above-described manufacturing process (with and without solvent exposure) are shown in FIG. 5. The release data clearly shows a drastic reduction of the burst and the release of the vitamin B₁₂ from the implants treated with methylene chloride.

Throughout this application, various publications are referenced. The disclosures of these publications in their entireties are hereby incorporated by reference into this application in order to more fully describe the compounds, compositions and methods described herein.

Various modifications and variations can be made to the compounds, compositions and methods described herein. Other aspects of the compounds, compositions and methods described herein will be apparent from consideration of the specification and practice of the compounds, compositions and methods disclosed herein. It is intended that the specification and examples be considered as exemplary. 

1.-33. (canceled)
 34. A delivery system comprising at least a first polymer and at least one agent, wherein the agent is dispersed in the first polymer, wherein the delivery system comprises at least two exposed surfaces of the first polymer, wherein at least one of the exposed surfaces or least one part of at least one exposed surface has surface morphology different than the other exposed surface or surfaces.
 35. The delivery system of claim 34, wherein the delivery system comprises a rod comprising two ends and a longitudinal surface, wherein the ends of the rod have a surface morphology that is different the surface morphology of the longitudinal surface.
 36. An article comprising a substrate coated with a polymer coating, wherein the polymer coating comprises at least two exposed surfaces, wherein at least one of the exposed surfaces or at least one part of at least one exposed surface has a surface morphology different than the other exposed surface or surfaces.
 37. The article of claim 36, wherein the article is in the form of a stent, suture, surgical clip, rod, pin, anchor, mesh, scaffold, tissue generating scaffold, medical electronic device, a wound dressing, a membrane, an orthopedic device for delivering an antibiotic or growth factor, a device for a dermal application for delivering an anesthetic or growth factor.
 38. The delivery system of claim 34, wherein all or a portion of the delivery system is coated with a second polymer forming a coated delivery system, wherein the coated delivery system comprises at least two exposed surfaces of the second polymer, and wherein at least one of the exposed surfaces or least one part of at least one exposed surface has surface morphology different than the other exposed surface or surfaces.
 39. The delivery system of claim 38, wherein the exposed surface has a surface morphology formed by a fluid treatment of the exposed surface.
 40. The delivery system of claim 39, wherein the exposed surface has a surface morphology formed by a fluid treatment of the exposed surface that comprises treating the exposed surface with a fluid that comprises methylene chloride, chloroform, acetone, anisole, ethylacetate, methylacetate, N-methyl-2-pyrrolidone, hexafluoro isopropanol, tetrahydrofuran, dimethylsulfoxide, water, 2-pyrrolidone, triethylcitrate, ethyl lactate, propylene carbonate, benzyl alcohol, benzyl benzoate, miglyol 810, isopropanol, ethanol, supercritical carbon dioxide, acetonitrile, water or a mixture thereof.
 41. The delivery system of claim 38, wherein the delivery system has the shape of a rod, a fiber, a cylinder, a beat, a ribbon, a disc, a wafer, or a free-formed shaped solid.
 42. The delivery system of claim 38, wherein the delivery system is a depot or implant.
 43. The delivery system of claim 38, wherein the first polymer comprises poly(lactide), poly(glycolide), poly(caprolactone), or a copolymer, mixture, or blend thereof.
 44. The delivery system of claim 38, wherein the second polymer comprises poly(lactide), poly(glycolide), poly(caprolactone), or a copolymer, mixture, or blend thereof.
 45. The delivery system of claim 38, wherein the agent comprises a bioactive agent.
 46. The delivery system of claim 38, wherein the bioactive agent comprises a drug, an immunological agent, an antigen, a protein, a peptide, an oligonucleotide, or a mixture thereof.
 47. The delivery system of claim 38, wherein the agent comprises an adhesive, a pesticide, a fragrance, an antifoulant, a dye, a salt, an oil, an ink, a cosmetic, a catalyst, a detergent, a curing agent, a flavor, a fuel, a herbicide, a metal, a paint, a photographic agent, a biocide, a pigment, a plasticizer, a propellant, a stabilizer, a polymer additive, or any combination thereof.
 48. The delivery system of claim 38, wherein the delivery system is partially coated and has been obtained by contacting only a portion of the exposed polymer with the fluid or by removing part of the polymer surface to expose untreated surface. 